The table set out in this Annex lists construction products and/or materials which satisfy all the requirements for the performance characteristic external fire performance without need for testing.
Classes of external fire performance for plastisol coated steel roof sheets
a External fire performance class as provided for in the table of the Annex to Decision 2001/671/EC. | |
Product | Classa |
---|---|
Plastisol coated steel roof sheets as specified below and when incorporated into a single layer or built-up roofing system as detailed below | BROOF (t1) BROOF (t2) BROOF (t3) |
Roofing sheets in accordance with EN 14782 and EN 14783, comprising profiled steel sheets, flat steel sheets or panels of coil coated galvanised or zinc-aluminium alloy coated steel of metal thickness ≥ 0,40 mm with an organic external (weather side) coating and, optionally, a reverse (internal) side organic coating. The external coating is of a liquid-applied Plastisol paint of maximum nominal dry film thickness 0,200 mm, a PCS of not greater than 8,0 MJ/m2 and a maximum dry mass of 330 g/m2. The reverse side organic coating (if any) has a PCS of not greater than 4,0 MJ/m2 and a maximum dry mass of 200 g/m2. Single-layer roofing system comprising a single skin, non-insulated roofing on a supporting structure (continuous or discrete supporting rails) of reaction to fire classification A2-s1, d0 or better. Built-up roofing system where the Plastisol coated steel roof sheets forms the external layer in a built-up assembly, where the supporting structure is of reaction to fire classification A2-s1, d0 or better and where immediately below the Plastisol coated steel sheet there is an insulating layer of reaction to fire classification A2-s1, d0 or better. This insulation shall be an un-faced mineral wool complying with EN 13162 and shall be glass fibre quilt of minimum density 10 kg/m3 (maximum nominal resin content 5 % by weight) and thickness ≥ 80 mm, or stone-wool of minimum density 25 kg/m3 (maximum nominal resin content 3,5 % by weight) and thickness ≥ 80 mm. Joints where the top sheeting includes joints these shall be as follows:
Sealants shall be of a butyl-mastic or similar with a nominal density of 1 500 to 1 700 kg/m3 applied as a continuous bead within the overlapped region of the joint at a rate of approximately 45 g/m length. Fixings where the roof sheets are fixed to the supporting construction using metal mechanical fixings adequate to provide structural stability to the roof construction with additional metal mechanical fixings used to ensure continuous intimate contact between the sheets and to provide watertight joints. |